4047 Solid Aluminum Welding MIG Wires

Introduction of 4047 Solid Aluminum Welding MIG Wires:
4047 Solid Aluminum Welding MIG Wires is an aluminum-silicon alloy welding wire containing about 12% silicon. It has good corrosion resistance, low melting point, good welding fluidity, and low deformation of the motherboard during welding. It is recommended for welding 1060, 1350, 3003, 3004, 5005, 5050, 6053, 6951, 7005 and other deformed aluminum alloys and cast aluminum 710.0 and 711.0.
 
1. Performance characteristics and uses: 4047 Solid Aluminum Welding MIG Wires is an aluminum welding wire containing 12% silicon, which is suitable for welding various cast and extruded aluminum alloys. Low melting point and good fluidity make the welding deformation of the base metal very small. It is used in welding or surfacing welding of light aluminum alloy processing industry; typical application fields are suitable for chemical, mold, furniture, container and other industries.
Second, the certification certificate: CE certification;
3. Specifications (mm): 0.8; 0.9; 1.0; 1.2; 1.6; 2.0; 2.4;
4. Packing of coiled welding wire: S100/0.5kg 11LB; S200/2kg; S300/6kg-7kg 16LB; S360/20kg.
Weld mechanical properties (reference value):
Tensile strength: 120-150MPa
Yield strength: 50-65MPa
Elongation: 10-18%
Conductivity: 42%IACS
Linear expansion coefficient: 22 10-6/K (20-100℃)
Melting temperature: 575～630℃
Chemical composition executive standard: GB/T3190-1998
Welding wire standard: GB10858-2008 equivalent to ANSI/AWS A5.10-92