4043 Aluminum TIG Welding Rod

Current Position :HOME/Welding Wire/4043 Aluminum TIG Welding Rod

ER4043 aluminum TIG welding  rod
 
ER4043 is a silicon containing 5% of aluminum silicon alloy welding Rod, good fluidity, heat cracking ability, but the lack of ductility. Because of the high silicon content, it is easy to produce the brittle Mg2Si in the weld, so that the plastic and corrosion resistance of the joints can decrease. In addition, the color of the surface of the weld is dark, and the color of the base material is different from that of the base metal.


 
Use: used as filling materials except aluminum magnesium alloy, aluminum alloy parts and castings and the gas welding argon arc welding. Welding used in the 6061 and 6000 series aluminum alloy, 3000 series and 2000 series aluminum alloy and cast aluminum. Widely used in railway locomotives, chemical, food and other industries.



Physical Property
Density 
kg/dm3
Melting temperature
 ℃
Thermal conductivity
 w/m•K
Linear expansion coefficient
 10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.67 573-625 163 22 42

Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
120--150 50--65 10--18

ER4043  Aluminium & Aluminium Alloy welding Rods
Classification GB/T 10858-2008············     HS 311
AWS A5.10··············       ER 4043
 
Typical composition in %
Si··················     4.50—5.50
Fe··················          <0.80
Cu···················      <0.30
Mn···················     <0.05
Mg···················     <0.05
Zn···················       <0.10
Be·················              <0.0003
Ti·················                <0.20
Others···············            <0.05
Others Total··········                   <0.15
 
Physical properties
(Approx.Values)
 0.2% yield strength Rpo2 (Mpa)····     40
 Tensile Strength Rm (Mpa)·····         120
Elongation A5 (L0=5d0) (%)······      8
 Test Temperature (℃)·····             20
 
Performance & Usage
 
 
This type containing 5% silicon,which can be adapted in welding all kinds of 
forging and casting alloys.With the good performance in anti-thermal crack.
Usage:ships,engine,mold,furniture,vessel,container,etc.
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG—Rods (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
TIG —rods(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
Rod Packagings Mig Rods:
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig Rod   :
5/10kg     ·······     length :1000mm



Note:
 
1. Al Si Rod while having a strong crack resistance, but plastic is poor, so after welding need plastic
deformation joints, should avoid using aluminum silicon Rod.
 
2 . The oxide and oil stain on the edge of the workpiece must be removed before welding.
 
3. Welding can be used to hold the molten metal plate, in order to ensure









 


CONTACT US
Contact
联系我们
Looking Forward to Your Response!

Tel:037155689814

Phone:086-13673369503

Fax:+86-371-55686475

Mobile:13673369503

Skype:Signialuminium

Email:frank@signialuminium.com

Address:A126 Building 4, No.89 Science Avenue,National HI-Tech Industry Development Zone,Zhengzhou,Henan

[UP]