5183 Aluminum TIG Welding Rod

Current Position :HOME/Welding Wire/5183 Aluminum TIG Welding Rod

ER5183 aluminum TIG welding  rod
 
ER5183 is a magnesium close to 5% and higher manganese content of aluminum magnesium welding Rod, with good corrosion resistance, heat resistance, high strength, good ductility. After the welding of the welding seam is still white, it can provide a good color for the welded joints. For some of the alloys, the strength of the welded joints is slightly higher than 5356.


 
Uses: used as a filler metal for argon arc welding of aluminum magnesium (3%Mg) alloy, which is used in the locomotive, chemical pressure vessel, nuclear industry, shipbuilding, refrigeration, boiler and aerospace industry.

Physical Property
Density 
kg/dm3
Melting temperature℃ Thermal conductivity
 w/m•K
Linear expansion coefficient 
10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.65 574-638 120 24.2 29

Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
275--300 125--140 15--20

ER5183 Aluminium & Aluminium Alloy welding Rods
 Classification GB/T 10858-2008   AWS A5.10····       ER 5183
 
Typical composition in %
Si···················      <0.40
Fe···················     <0.40
Cu···················     <0.10
Mn·················         0.05—1.00
Mg·················         4.30—5.20
Cr·················          0.05—0.25
Zn··················          <0.25
Be··················          <0.0003
Ti··················            <0.15
Others··············                 <0.05
Others Total·········                        <0.15
 
Physical properties
(Approx.Values)
 0.2% yield strength Rpo2 (Mpa)····       125
 Tensile Strength Rm (Mpa)·····           275
Elongation A5 (L0=5d0) (%)······        17
Test Temperature (℃)······           20
 
Performance & Usage
 
This type of product is widely used in general welding material with the Mg of 
4.5%, which can be used in jointing or overlay forging and casting alloys 
processing in the same grade. Usage:pressure vessel,nuclear,ship-building,boiler,space industry ,etc .
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG — Rods (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
TIG — rods(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
 
Rod Packagings
Mig Rods:
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig Rod :
5/10kg     ·······     length :1000mm



Note :

 
1. The Rod should not be at operating temperature greater than 65 degrees of aluminum alloy structure
in use, because in the ambient temperature in welding joint reply Esheng stress corrosion cracking.
 
2. Welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will
cause welding seam welding and cause the hole, slag and other defects.
 
3. Welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid
hot crack.








CONTACT US
Contact
联系我们
Looking Forward to Your Response!

Tel:037155689814

Phone:086-13673369503

Fax:+86-371-55686475

Mobile:13673369503

Skype:Signialuminium

Email:frank@signialuminium.com

Address:A126 Building 4, No.89 Science Avenue,National HI-Tech Industry Development Zone,Zhengzhou,Henan

[UP]