5356 ALuminum MIG Welding Wire

Current Position :HOME/Welding Wire/5356 ALuminum MIG Welding Wire

ER5356 aluminum TIG welding  wire
 
ER5356 is a magnesium alloy with magnesium 5% and a small amount of titanium refined aluminum alloy welding wire, with good corrosion resistance, high heat resistance, high strength, good ductility. Weld anodizing treatment is still white, can provide a good match for welded joints, is a widely used general consumables.


 
Uses: aluminum magnesium (3%Mg) alloy argon arc welding of the most basic metal filler metal, in the aluminum silicon magnesium, aluminum magnesium alloy welding and aluminum magnesium alloy castings were also used in welding. Such as the carriages, chemical pressure vessel, bicycles, aluminum plate and other sports equipment and ordnance pwireuction, shipbuilding, aviation and other industries.



Physical Property
Density 
kg/dm3
Melting temperature ℃ Thermal conductivity
 w/m•K
Linear expansion coefficient
 10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.65 575-633 120 24.1 29

Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
250--300 110--140 15--25

ER5356   Aluminium & Aluminium Alloy welding wire
 Classification GB/T 10858-2008············       HS 331
AWS A5.10··············       ER 5356
 
Typical composition in %
Si··················          <0.25
Fe··················         <0.40
Cu··················         <0.10
Mn·················        0.05—0.20
Mg···············                4.50—5.50
Cr·················         0.05—0.20
Zn··················          <0.10
Be···············                      <0.0003
Ti················              0.06—0.20
Others···············            <0.05
Others Total··········                   <0.15
 
Physical properties
(Approx.Values)
 0.2% yield strength Rpo2 (Mpa)···        110
 Tensile Strength Rm (Mpa)·····           240 Elongation A5 (L0=5d0) (%)···· 17
 Test Temperature (℃)·····               20
 
Performance & Usage
 
This type of pwireuct is widely used in general welding material with the Mg 
of 5%, which can be used in jointing or overlay forging and casting alloys 
processing. And the pwireuct is of high toughness , good forgeability, and 
well anti-comosiveness.
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG—wires (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
 
TIG —wires(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
wire Packagings  Mig wires :
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig wire  :
5/10kg     ·······     length :1000mm



Note :
 
1. The welding wire is not used in the structure of aluminum alloy, which is more than 65 degrees, because
in the above mentioned temperature, the stress corrosion cracking of the welded joints.
 
2. Welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will cause
welding seam welding and cause the hole, slag and other defects.
 
3. Welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid hot crack.


 




 


CONTACT US
Contact
联系我们
Looking Forward to Your Response!

Tel:037155689814

Phone:086-13673369503

Fax:+86-371-55686475

Mobile:13673369503

Skype:Signialuminium

Email:frank@signialuminium.com

Address:A126 Building 4, No.89 Science Avenue,National HI-Tech Industry Development Zone,Zhengzhou,Henan

[UP]