ER1070 Aluminum MIG Welding Wire

Current Position : Home/Welding Wire/ ER1070 Aluminum MIG Welding Wire

ER1070 Aluminum MIG Welding Wire

Author:  Time:2023-05-18
ER1070 Aluminum MIG Welding Wire

Detail


ER1070 aluminum MIG welding wire
 
ER1070 is pure aluminum wire with aluminum content ≥99.7% and has good corrosion resistance,
high thermal conductivity and conductive performance and excellent processing properties. However,
the strength of the low.
 
Uses: used as pure aluminum of argon arc welding and gas welding filler material, widely used in
electrolytic aluminium bus bar and a guide wire connection and electric power, chemical, food etc. industries.


Physical Property
Density kg/dm3 Melting temperature ℃ Thermal conductivity
 w/m•K
Linear expansion 
coefficient 10¯6/K(20-100℃)
Electric conductivity
 % IACS
2.7 647-685 210-230 23.5 60

Weld Mechanical Properties (reference value)
Tension Strength(MPa) Yield Strength(MPa) Elongation (%)
60-80 40-60 25-35

      ER1070  Aluminium & Aluminium Alloy welding wires
Classification GB/T 10858-2008  AWS A5.10 ····       ER 1070
 
Typical composition in %
Si················            <0.2
Fe················            <0.25
Cu·················       0.04
Mn·················            <0.03
Mg·················            <0.03
Zn··················         <0.04
Ti··················         <0.03
Al··················          99.7%

 
 
Physical properties
(Approx.Values)
1.Appearance: bright surface of welding wire without oil, 
coarse surface and other unclean mark.
2.Welding performance: Feeding well, molding well with little spatter,
low noise and improvement in the quality of welding.
3.Melting range:647-658℃.
4.Bulk density: 2.7kg/dm3.
5.tensile strength:60-80MPa.
6.yield strength:40-60MPa.
 
Performance & Usage
 
It is used for pure aluminum material as a filler wire in argon ARC welding and
 gas welding, such as electrolytic aluminum plant, electricity industry, chemical 
industry, food industry, etc.
Shielding gas Argon, Helium, or Argon/Helium—mixtures.
Dimensions Φ MIG—wires (mm):
0.8 ; 0.9 ; 1.0 ; 1.2 ; 1.6 ; 2.0 ; 2.4
 
TIG —wires(mm):
1.6 ; 2.0 ; 2.4 ; 3.2 ; 4.0 ; 5.0 ; 6.0
wire Packagings Mig wires :
 
S100/0.5kg 1Lb , S200/2kg , S270-S300/6kg-7kg
Tig wire ) :
 
5/10kg     ·······     length :1000mm

Note: 
1.welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will cause
welding seam welding and cause the hole, slag and other defects.
2 welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid hot crack.



CONTACT US
CONTACT US
Looking Forward to Your Response!

Mobile:86 17344894490

Email:inquiry@signialuminium.com

Address:A126 Building 4, No.89 Science Avenue,National HI-Tech Industry Development Zone,Zhengzhou,Henan